Modell: Heat Shrink Tube
Property |
Test Method |
Typical Value |
Tensile Strength |
ASTM D 2671 |
18 MPa |
Ultimate Elongation |
ASTM D 2671 |
700 % |
Density |
ISO R1183 D |
0.94 g/cm2 |
Dielectric Strength |
IEC243 |
20KV/mm |
Dielectric Constant |
IEC243 |
2.5 max. |
Longitudinal Change |
ASTM D 2671 |
0±5% |
Part No. |
OD after Recovery (MM) |
Length(mm) |
Fusion tube(D) |
Steel rod(D) |
||
ID (MM) |
Length (MM) |
OD (MM) |
Length (MM) |
|||
Larger Sleeves | ||||||
JFSP-60 |
3.1±0.1 |
60 |
1.4 |
60 |
1.5 |
55 |
JFSP-60B |
2.9±0.1 |
60 |
1.3 |
60 |
1.5 |
56 |
JFSP-45 |
3.1±0.1 |
45 |
1.4 |
45 |
1.5 |
40 |
JFSP-40 |
3.1±0.1 |
40 |
1.4 |
40 |
1.5 |
36 |
JFSP-23 |
3.1±0.1 |
23 |
1.4 |
23 |
1.5 |
18 |
Standard Sleeves | ||||||
JFSP-61M |
2.7±0.1 |
61 |
1.3 |
61 |
1.2 |
55 |
JFSP-60M |
2.7±0.1 |
60 |
1.3 |
60 |
1.2 |
56 |
JFSP-45M |
2.7±0.1 |
45 |
1.3 |
45 |
1.2 |
40 |
JFSP-40M |
2.7±0.1 |
40 |
1.3 |
23 |
1.2 |
36 |
JFSP-30M |
2.7±0.1 |
30 |
1.3 |
23 |
1.2 |
26 |
JFSP-25M |
2.7±0.1 |
25 |
1.3 |
23 |
1.2 |
21 |
Mini Sleeves | ||||||
JFSP-40T-S |
1.5±0.1 |
40 |
0.5 |
40 |
0.7 |
40 |
JFSP-40TS |
1.9±0.1 |
40 |
1.0 |
40 |
0.7 |
40 |
JFSP-60T |
2.0±0.1 |
60 |
0.5 |
60 |
1.0 |
56 |
JFSP-40T |
2.0±0.1 |
40 |
0.5 |
40 |
1.0 |
36 |
JFSP-60A |
2.5±0.1 |
60 |
1.3 |
60 |
1.0 |
56 |
JFSP-45A |
2.5±0.1 |
45 |
1.3 |
45 |
1.0 |
41 |
JFSP-40A |
2.5±0.1 |
40 |
1.3 |
40 |
1.0 |
36 |
Micro Sleeve | ||||||
JFSP-40S |
1.3±0.1 |
40 |
0.5 |
40 |
0.5 |
40 |
JFSP-25S |
1.3±0.1 |
25 |
0.5 |
25 |
0.5 |
25 |
JFSP-25SS |
1.2±0.1 |
25 |
0.4 |
25 |
0.5 |
25 |
JFSP-18S |
1.3±0.1 |
18 |
0.5 |
18 |
0.5 |
18 |
JFSP-15S |
1.3±0.1 |
15 |
0.5 |
15 |
0.5 |
15 |
JFSP-10S |
1.3±0.1 |
10 |
0.5 |
10 |
0.5 |
10 |
Produktgruppe : Andere Panel